Cynnwys Ferro Niobuim
Gadewch neges
Cynnwys pf Ferro Niobuim
|
Gradd |
cyfansoddiad ％ | |||||||||||||||
| Ds | Diolch | Al | Os | C | S | P | W | Ti | Cu | Mn | Fel | Sn | Mae sb | Pb | Bi | |
| Llai na neu'n hafal i | ||||||||||||||||
| FeNb70 | 70-80 | 0.8 | 3.8 | 1.5 | 0.04 | 0.03 | 0.04 | 0.3 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60—A | 60-70 | 0.5 | 2.0 | 0.4 | 0.04 | 0.02 | 0.02 | 0.2 | 0.2 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60% e2% 80% 94B | 60-70 | 0.8 | 2.0 | 1.0 | 0.05 | 0.03 | 0.05 | 0.2 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50% e2% 80% 94A | 50-60 | 0.8 | 2.0 | 1.2 | 0.05 | 0.03 | 0.05 | 0.1 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50% e2% 80% 94B | 50-60 | 1.5 | 2.0 | 4.0 | 0.05 | 0.03 | 0.05 | |||||||||
Ferro Niobiumyn sylwedd ychwanegol i'r weithdrefn cynhyrchu metelau aneglur a bydd yn rhoi ychydig o briodweddau hudolus i'r cyfansoddyn dilynol. Un o fanteision hanfodol ychwaneguFerro Niobiumi amalgam yn ei gelyn o eiddo dinistriol (yn well nag unrhyw beth dur carbon). Ar ben hynny, gall ychwanegu Ferro Niobium at gyfuniad ei gwneud yn gynyddol weldadwy a llawer mwy sylfaen. Gydag ehangu gwahanol gydrannau, er enghraifft, mae dur a grëir gan Zirconium, Ferro Niobium yn ddelfrydol ar gyfer cymwysiadau cyfeiriadol cain, er enghraifft, rhychwantau atal. Mae Ferro Niobium yn ehangu gwrthwynebiad tymheredd uchel, rhwystr defnydd, rhwystr ocsideiddio, gwrthwynebiad ymgripiad, yn union fel lleihau dadelfennu ar dymheredd uwch.
ZHEN AN CO RHYNGWLADOL, LTD
Symudol: +86-18211636583(whatsapp/wechat)
Ffacs: +86-372-5055180
Email:kay@zaferroalloy.com
Gwefan: https://www.zaferroalloy.cn/
Prif swyddfa: Swyddfa Huafu, Dinas Anyang, Talaith Henan, Tsieina